Thermoplastic comparison
PHB (polyhydroxybutyrate, a PHA) vs PVDF (polyvinylidene fluoride)
Every value below is a typical room-temperature figure with its source, test method and conditions — the same dataset that drives the calculators.
| Property | PHB (polyhydroxybutyrate, a PHA) | PVDF (polyvinylidene fluoride) | Difference |
|---|---|---|---|
| Density | 1.25 g/cm³ | 1.78 g/cm³ | PVDF (polyvinylidene fluoride) — 42% higher |
| Young's modulus E | 3.5 GPa | 2 GPa | PHB (polyhydroxybutyrate, a PHA) — 75% higher |
| Tensile strength | 40 MPa | 45 MPa | PVDF (polyvinylidene fluoride) — 13% higher |
| Glass transition Tg | 4 °C | -35 °C | PHB (polyhydroxybutyrate, a PHA) — 39 °C higher |
| Melting point Tm | 177 °C | 170 °C | PHB (polyhydroxybutyrate, a PHA) — 7 °C higher |
Where these numbers come from
- Sudesh, Abe & Doi, Prog. Polym. Sci. 25 (2000) 1503–1555 — PHA structure & properties review
- CAMPUS plastics database — typical grade datasheet values (campusplastics.com)
Typical room-temperature values for learning and preliminary design; grades vary widely and a supplier datasheet always overrides a textbook figure. Confirm against the datasheet before design work.