Thermoplastic comparison
PHB (polyhydroxybutyrate, a PHA) vs Polysulfone (PSU)
Every value below is a typical room-temperature figure with its source, test method and conditions — the same dataset that drives the calculators.
| Property | PHB (polyhydroxybutyrate, a PHA) | Polysulfone (PSU) | Difference |
|---|---|---|---|
| Density | 1.25 g/cm³ | 1.24 g/cm³ | PHB (polyhydroxybutyrate, a PHA) — 1% higher |
| Young's modulus E | 3.5 GPa | 2.5 GPa | PHB (polyhydroxybutyrate, a PHA) — 40% higher |
| Tensile strength | 40 MPa | 70 MPa | Polysulfone (PSU) — 75% higher |
| Glass transition Tg | 4 °C | 185 °C | Polysulfone (PSU) — 181 °C higher |
Where these numbers come from
- Sudesh, Abe & Doi, Prog. Polym. Sci. 25 (2000) 1503–1555 — PHA structure & properties review
- CAMPUS plastics database — typical grade datasheet values (campusplastics.com)
Typical room-temperature values for learning and preliminary design; grades vary widely and a supplier datasheet always overrides a textbook figure. Confirm against the datasheet before design work.