PEI (Ultem) vs PPS (polyphenylene sulfide)
Every value below is a typical room-temperature figure with its source, test method and conditions — the same dataset that drives the calculators.
| Property | PEI (Ultem) | PPS (polyphenylene sulfide) | Difference |
|---|---|---|---|
| Density | 1.27 g/cm³ | 1.35 g/cm³ | PPS (polyphenylene sulfide) — 6% higher |
| Young's modulus E | 3.2 GPa | 3.8 GPa | PPS (polyphenylene sulfide) — 19% higher |
| Tensile strength | 105 MPa | 80 MPa | PEI (Ultem) — 31% higher |
| Glass transition Tg | 217 °C | 90 °C | PEI (Ultem) — 127 °C higher |
Where these numbers come from
- CAMPUS plastics database — typical grade datasheet values (campusplastics.com)
Typical room-temperature values for learning and preliminary design; grades vary widely and a supplier datasheet always overrides a textbook figure. Confirm against the datasheet before design work.