| Property | LCP (liquid crystal polymer) | Polyamide 12 (PA12, Nylon 12) | Difference |
|---|---|---|---|
| Density | 1.4 g/cm³ | 1.01 g/cm³ | LCP (liquid crystal polymer) — 39% higher |
| Young's modulus E | 10.6 GPa | 1.4 GPa | LCP (liquid crystal polymer) — 7.6× higher |
| Tensile strength | 182 MPa | 50 MPa | LCP (liquid crystal polymer) — 3.6× higher |
| Melting point Tm | 280 °C | 178 °C | LCP (liquid crystal polymer) — 102 °C higher |
Where these numbers come from
- Celanese Vectra A950 liquid crystal polymer datasheet, typical (flow-direction) values
- CAMPUS plastics database — typical grade datasheet values (campusplastics.com)
Typical room-temperature values for learning and preliminary design; grades vary widely and a supplier datasheet always overrides a textbook figure. Confirm against the datasheet before design work.